| Waiwai | Unite | ʻano hoʻāʻo | Kūlana |
| Kaha laina | ʻO Tex | ASTM D1907 | 2400±10% |
| Ka ikaika uʻi 1) haki 2) LASE 0.3% 3) LASE0.5% 4) LASE1.0% | N | ASTM D 885 | Min.1200 Min.192 Min.240 Min.640 |
| Pākuʻi | g/cm³ | ASTM D1505 | 2.55±0.05 |
| Modulus opio | Gpa | ASTM D885,D76 | Min.62.5 |
| Elongation i ka wā hoʻomaha | % | ASTM D885 | 1.7-3.0 |
| ʻO ka māmā holo | % | Min 150 | |
| Hiki ke hoʻoheheʻe | % | Min 200 | |
| ʻAno wai | % | ʻAno ālai wai | ≤1 |
| ʻAno ālai wai ʻole | ≤05 | ||
| ʻŌlelo | ʻO ka absorption no ke ʻano pale wai wale nō | ||